RANCANG BANGUN MESIN ELEKTROPLATING PORTABLE BERBASIS ARDUINO UNTUK PELAPISAN LOGAM PRESISI

Abstrak

Penelitian ini bertujuan untuk merancang, membuat, dan menguji unjuk kerja mesin elektroplating portabel berbasis Arduino untuk pelapisan logam presisi. Mesin dirancang dengan mengintegrasikan sistem kontrol berbasis Arduino, digital timer, power supply DC, sensor suhu, relay, panel kontrol, serta komponen pendukung lainnya sehingga mampu mengendalikan parameter proses elektroplating secara lebih praktis dan konsisten. Metode penelitian yang digunakan adalah metode kuantitatif dengan pendekatan eksperimen laboratorium. Variabel bebas dalam penelitian ini meliputi variasi kuat arus sebesar 3 A, 6 A, dan 9 A serta waktu pelapisan selama 10, 15, dan 20 menit. Variabel terikat berupa kualitas lapisan hasil elektroplating berdasarkan kerataan dan daya lekat lapisan, sedangkan variabel terkontrol meliputi jenis larutan elektrolit, material benda kerja SS400, dan jarak anoda–katoda 100 mm. Data diperoleh melalui pengujian langsung dan dokumentasi visual hasil pelapisan pada setiap variasi perlakuan. Hasil penelitian menunjukkan bahwa mesin elektroplating portabel berbasis Arduino berhasil direalisasikan dan mampu beroperasi sesuai dengan fungsi yang dirancang. Variasi parameter proses memberikan pengaruh terhadap kualitas lapisan logam yang dihasilkan. Kombinasi arus 6 A dengan waktu pelapisan 20 menit menghasilkan kualitas pelapisan terbaik dengan lapisan yang lebih merata, permukaan relatif halus, memiliki tingkat kilap yang baik, dan daya lekat yang optimal dibandingkan variasi lainnya. Dengan demikian, mesin yang dikembangkan layak digunakan sebagai media pembelajaran, penelitian, dan pengembangan proses elektroplating pada skala laboratorium maupun industri kecil.

This study aims to design, fabricate, and evaluate the performance of an Arduino-based portable electroplating machine for precision metal coating. The machine was developed by integrating an Arduino-based control system, digital timer, DC power supply, temperature sensor, relay, control panel, and supporting components to provide practical and consistent control over the electroplating process. The research employed a quantitative method with a laboratory experimental approach. The independent variables were electrical current variations of 3 A, 6 A, and 9 A, and plating durations of 10, 15, and 20 minutes. The dependent variables were the coating quality, evaluated based on surface uniformity and adhesion, while the controlled variables included the electrolyte solution type, SS400 low-carbon steel workpiece, and an anode-to-cathode distance of 100 mm. Data were collected through experimental testing and visual documentation of the coating results for each treatment variation. The results indicate that the Arduino-based portable electroplating machine was successfully developed and functioned according to its design specifications. The electroplating parameters significantly affected the quality of the deposited coating. The combination of a 6 A current and a 20-minute plating time produced the best coating quality, characterized by superior uniformity, a relatively smooth surface, optimal luster, and strong adhesion compared to other variations. Therefore, the developed machine is suitable for educational purposes, laboratory-scale research, and small-scale industrial applications.